Assembly and programming of an electronic measurement device that allows to perform materials characterization in space on student satellite ESTCube-2. (EST: Mõõteseadme valmistamine ja programmeerimine materjaliuuringute jaoks kosmoses tudengisatelliidil ESTCube-2). This electronic device is one of the two major components in our developed corrosion testing module, which will be used to test a novel nanostructured coating and a smart radiation shielding material in LEO (Low Earth Orbit).
The preparation, programming and preliminary testing of the electronic measurement device is carried out by Hedgehog OÜ and funded by Captain Corrosion OÜ (30%) and Enterprise Estonia (70%).
ESTCube group assists us with the planning of this experiment and with the integration of our corrosion testing module to the student satellite ESTCube-2. Once the satellite is in space, we will also carry out the tests together.
Laboratory of Thin Film Technology (University of Tartu) is our main partner for assembling the test system as well as other prototypes, that will be used to test the patented nanostructured coating. With them we also carry out laboratory-based materials characterization measurements and tests.
We are currently making a science video series about scanning electron microscopy studies. In these videos we discuss the sample preparation and show how things actually look like in the microscopic scale.
Videos can be seen in our YouTube channel.
The scanning electron microscopy images made in these studies are uploaded to our gallery.
We just published one of our most sophisticated videos made so far. It is about corrosion in space due to radiation and in the video we will discuss different radiation-matter interactions.
Graphene – a novel material, that consists of only a single layer of oriented carbon atoms. This material is hundreds times stronger than steel and conducts heat and electricity with exceptional efficiency. A perfect sheet of graphene could actually be so strong that it could lift even a kitten! But can this one atom thick material also be the thinnest corrosion resistant coating ever made? There have been several papers over the last decade discussing this possibility and this peaked our interest. So we first prepared graphene on larger copper substrates by chemical vapor deposition (CVD). Following Raman spectroscopy and scanning electron microscopy (SEM) studies confirmed, that we had a single layer of high quality graphene, that coated the whole substrate. Now it was time to test how well this single atom thick coating can protect the underlying copper from corrosion – for that we used chemical and electrochemical methods. According to electrochemical tests, graphene actually seemed to slow down the corrosion, but additional high resolution imaging with the scanning electron microscope revealed the terrifying truth!
Graphene had started to delaminate and the areas with exposed copper had suffered severe corrosion, unlike bare copper substrates, that corroded uniformly. This severe type of copper corrosion in the defects of graphene was actually caused by graphene itself because of localized galvanic corrosion. In this galvanic couple the large area of highly conductive graphene served as a cathode and the small area of exposed copper as an anode. As a result the copper was continuously stripped from electrons, causing it to easily react with the corrosive environment. So basically it was clear that graphene may initially seem to be a corrosion resistant barrier, but eventually the graphene coated substrate would suffer much more damage than the uncoated substrate! Also, it is impossible to create a large area graphene that has no defects where chloride ions wouldnt be able to slip through. However, it was also true that if the defects in graphene were to be fixed, the galvanic couple and corrosion would be undone. In our laboratory we sealed these small defects in graphene by electrodeposition of polypyrrole. Surprisingly this polymer deposited extremely well on such defects, sealing even holes that were several microns wide. As a result we obtained a nanocomposite coating, that consisted of graphene and polypyrrole. This coating performed well both in chemical and electrochemical corrosion tests.
So what did we learn from all this? The first thing that we learned was the fact that galvanic corrosion can effectively be stopped even at nano-scale, by blocking one of its driving reactions. Second, we discovered that the electrochemical behavior of the defects of graphene is completely different from the defect free area. Third, we realised that polypyrrole may even visualize the quality of graphene for the naked eye because polypyrrole deposits only on graphene and its defects but not on copper if the defects were too big. For example if one built a CVD (chemical vapour deposition) reactor for the preparation of 1 square meter of graphene on a copper foil, then there is a need to somehow see if the foil was actually evenly coated by graphene. By depositing polypyrrole on the graphene coated copper substrate, it is possible to see even with the naked eye if the whole substrate turns black or of there are brigher areas. If there were brighter areas on this copper foil with graphene and polypyrrole, then this would mean that in those regions we dont actually have graphene where polypyrrole could deposit. This would mean that either the gas flow or temperature in the CVD process had not been ideal.
Although things get complicated in the nano-scaled world, the processes are still governed by a set of rules. One day we’ll figure them all out and then we can truly play „dice“ at the atomic scale!